Nerjaveèi klas 316 - Endistriyèl Kowozyon Rezistan
Feb 05, 2026
Kite yon mesaj
Konpozisyon
Tablo 1.Ranje konpozisyon pou 316 klas nan asye pur.
| Klas | C | Mn | Si | P | S | Kr | Mo | Ni | N | |
|---|---|---|---|---|---|---|---|---|---|---|
| 316 | Min | - | - | - | 0 | - | 16.0 | 2.00 | 10.0 | - |
| Max | 0.08 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
| 316L | Min | - | - | - | - | - | 16.0 | 2.00 | 10.0 | - |
| Max | 0.03 | 2.0 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | 0.10 | |
| 316H | Min | 0.04 | 0.04 | 0 | - | - | 16.0 | 2.00 | 10.0 | - |
| max | 0.10 | 0.10 | 0.75 | 0.045 | 0.03 | 18.0 | 3.00 | 14.0 | - |
Pwopriyete mekanik
Tablo 2.Pwopriyete mekanik nan 316 klas asye pur.
| Klas | Tensile Str (MPa) min | Sede Str 0.2% Prèv (MPa) min | Long (% nan 50 mm) min | Dite | |
|---|---|---|---|---|---|
| Rockwell B (HR B) max | Brinell (HB) max | ||||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
Remak: 316H gen tou yon egzijans pou yon gwosè grenn ASTM non . 7 oswa pi grosye.
Pwopriyete Fizik
Tablo 3.Pwopriyete fizik tipik pou asye pur klas 316.
| Klas | Dansite (kg/m3) | Modil elastik (GPa) | Mwayèn Ko-efè ekspansyon tèmik (µm/m/ degre) | Kondiktivite tèmik (W/mK) | Espesifik Chalè 0-100 degre (J/kg.K) | Rezistans elektrik (nΩ.m) | |||
|---|---|---|---|---|---|---|---|---|---|
| 0-100 degre | 0-315 degre | 0-538 degre | Nan 100 degre | Nan 500 degre | |||||
| 316/L/H | 8000 | 193 | 15.9 | 16.2 | 17.5 | 16.3 | 21.5 | 500 | 740 |
Voye rechèch