630 (1.4542) Nerjaveèi asye . 630 Nerjaveèi asye se youn nan dènye klas asye pur yo te jwenn nan ane 1960 yo. Klas sa a ekri tankou 1.4542 oswa x5crnicunb16-4 oswa 17-4 pH dapre EN Norm epi li ekri kòm UNS S17400 dapre UNS Norm.
17-4PH Materyèl Klas ekivalan
| AISI 630 | ASTM A693 (630) | AMS 5342 | Mil-s-81506 |
| AMS 5604 | ASTM A705 (630) | AMS 5343 | SAE J467 (17-4ph) |
| AMS 5622 | MIL C-24111 | AMS 5344 | Asme SA705 |
| AMS 5643 | MIL P-47183 | AMS 5355 | Asme sa564 |
| ASTM A564 (630) | MIL S-81591 | AMS 5825 |
|
Ki konpozisyon 1.4542 materyèl?
| Pwa % | C | Mn | P | S | Si | Cr | NI | Mwa | CU | Nb+ta |
| Min. | 15,0 | 3,50 | 3,00 | 0,15 | ||||||
| Max. | 0,070 | 1,00 | 0,040 | 0,030 | 0,70 | 17,5 | 5,00 | 0,60 | 5,00 | 0,45 |
Pwopriyete mekanik (espesifik pou ba - kondisyon H1150D)
| Kondisyon | |||||||||
| 17-4ph Rkant |
17-4ph (H900) |
17-4ph (H925) |
17-4ph (H1025) |
17-4ph (H1075) |
17-4ph (H1100) |
17-4ph (H1150) |
17-4ph (H1150+ H1150, doub ki gen laj) |
17-4ph (H1150M) |
|
| Fòs rupture N/mm2 | 1034 | 1380 | 1310 | 1170 | 1140 | 1035 | 1000 | 965 | 860 |
| 0.2% ys N/mm2 | 760 | 1275 | 1200 | 1140 | 1035 | 930 | 860 | 760 | 585 |
| Rediksyon nan zòn % | 30-60 | 50 | 54 | 56 | 58 | 58 | 60 | 60 | 68 |
| Elongasyon % | 6-15 | 14 | 14 | 15 | 16 | 17 | 19 | 20 | 22 |
| Charp Enpak J |
20 | 34 | 47 | 54 | 61 | 68 | 108 | 135 | |
Tretman solisyon pou UNS S17400 asye pur
| Kondisyon | Bese | Bese | Kalite refwadisman | Rez nan | |
| Tanperati | Tan | Brinell | Rockwell C | ||
| 17-4ph rkwit | 1038C | 1/2 | Lwil/lè (anba 32 degre) | 363 Max. | 39 Max. |
| 17-4phh900 | 480 degre | 1 | Lè | 420 | 44 |
| 17-4phh925 | 594C | 4 | Lè | 409 | 42 |
| 17-4PHH1025 | 55 degre | 4 | Lè | 352 | 38 |
| 17-4phh1075 | 85C | 4 | Lè | 341 | 36 |
| 17-4phh1100 | 595 degre | 4 | Lè | 332 | 35 |
| 17-4phh1150 | 621 degre | 4 | Lè | 311 | 33 |
| 17-4ph (H 1150+ H1150, doub ki gen laj H1150) | 760 degre 760 degre |
4 ki te swiv pa 4 |
Lè Lè |
302 | 33 |
| 17-4PH (H1150-M) | 760 degre 620 degre |
2 ki te swiv pa 4 |
Lè Lè |
277 | 27 |
Tretman chalè
Solisyon rkwit nan 1040 degre. Double fè tèt di toujou/ ki gen laj nan 620 degre (1150 degre F).
Soudedabilite
Pratik bon, pre-chofaj ak pòs-chofaj yo itilize pou klas estanda ki di ki pa obligatwa.
Fleksibilite chalè-trete:
Atravè divès kalite tretman chalè (egzanp, H900, H1025, H1150), fòs li yo ak andirans ka siyifikativman ajiste nan kostim kondisyon aplikasyon divès.
Gnee espesyalize nan pwodiksyon an ak fabrike nan 17-4ph asye pur nan divès fòm, ki gen ladan plak, ba, tib, fil ak forgings, ki yo lajman itilize nan avyon, chimik, lwil oliv ak gaz ak lòt endistri yo. Nou sipòte k ap travay frèt, k ap travay cho, soude, pwosesis retounen ak lòt tretman pwosesis, ak bay yon varyete moun rich nan martensitic asye pur klas.Email:sales@gneestainless.com