Premium AISI 304H Nerjaveèi soti nan Gnee
Mar 23, 2026
Kite yon mesaj
🧪 Konpozisyon Chimik
| Eleman | Konpozisyon (%) |
|---|---|
| Kabòn (C) | 0.04 - 0.10 |
| Manganèz (Mn) | Mwens pase oswa egal a 2.00 |
| Silisyòm (Si) | Mwens pase oswa egal a 0.75 |
| Fosfò (P) | Mwens pase oswa egal a 0.045 |
| Souf (S) | Mwens pase oswa egal a 0.030 |
| Kwòm (Cr) | 18.0 - 20.0 |
| Nikèl (Ni) | 8.0 - 10.5 |
| Azòt (N) | Mwens pase oswa egal a 0.10 |
| Fè (Fe) | Balans |
⚙️ Pwopriyete mekanik
| Pwopriyete | Valè |
|---|---|
| Fòs rupture (min) | 515 MPa |
| Sede fòs 0.2% Offset (min) | 205 MPa |
| Elongasyon nan 50mm (min) | 40% |
| Rediksyon nan zòn (min) | 50% |
| Dite (Brinell) | Mwens pase oswa egal a 201 HB |
| Dite (Rockwell B) | Mwens pase oswa egal a 92 HRB |
| Enèji enpak (Charpy V-nan 20 degre) | Pi gran pase oswa egal a 120 J |
| Limit fatig (10 ^ 7 sik) | 240 MPa |
| Modil Elastisite | 200 GPa |
🔬 Pwopriyete Fizik
| Pwopriyete | Valè |
|---|---|
| Dansite | 8.00 g/cm³ |
| Pwen k ap fonn | 1400-1450 degre |
| Kondiktivite tèmik (nan 100 degre) | 16.2 W/m·K |
| Koyefisyan ekspansyon tèmik (20-100 degre) | 17.2×10-6/K |
| Kapasite Chalè Espesifik | 500 J/kg·K |
| Rezistans elektrik (nan 20 degre) | 0.72 µΩ·m |
| Pèmeyabilite mayetik | 1.02 (Non-mayetik) |
| Difizyon tèmik | 4.2×10-6 m²/s |
| Tanperati Curie | N/A (Austenitic) |
📏 Espesifikasyon pwodwi yo
| Spesifikasyon | Opsyon ki disponib |
|---|---|
| Fòm pwodwi | Plak, fèy, bobin, ba, baton, tib, tiyo, forgings |
| Plak epesè | 6mm - 200mm |
| Epesè fèy | 0.4mm - 6mm |
| Dyamèt Bar | 6mm - 300mm |
| Dyamèt Eksteryè Tib | 6mm - 610mm |
| Estanda | ASTM A240, A479, A312, EN 10088-2, JIS G4305, GB/T 3280 |
| Sifas fini | 2B, BA, No.4, HL (Hairline), glas, marinated |
| Tolerans | ± 0.1mm (epesè), ± 3mm (lajè), ± 6mm (longè) |
| Kondisyon Edge | Mill Edge, Slit Edge, Taye Edge |
| Tretman Chalè | Solisyon rkwit (1040-1120 degre) |