AISI 321H Segondè Kabòn Estabilize Nerjaveèi

🧪 Konpozisyon Chimik

Eleman	Konpozisyon (%)
Kabòn (C)	0.04 - 0.10
Manganèz (Mn)	Mwens pase oswa egal a 2.00
Silisyòm (Si)	Mwens pase oswa egal a 0.75
Fosfò (P)	Mwens pase oswa egal a 0.045
Souf (S)	Mwens pase oswa egal a 0.030
Kwòm (Cr)	17.0 - 20.0
Nikèl (Ni)	9.0 - 13.0
Titàn (Ti)	4 × (C + N) min, 0.70 max
Azòt (N)	Mwens pase oswa egal a 0.10
Fè (Fe)	Balans

⚙️ Pwopriyete mekanik

Pwopriyete	Valè
Fòs rupture (tanperati chanm)	Pi gran pase oswa egal a 515 MPa
Fòs Sede (0.2% Offset)	Pi gran pase oswa egal a 205 MPa
Elongasyon (50mm kalib)	Pi gran pase oswa egal a 40%
Rediksyon nan zòn	Pi gran pase oswa egal a 50%
Dite (Brinell)	Mwens pase oswa egal a 217 HB
Enèji enpak (Charpy V-dan, Tanperati chanm)	Pi gran pase oswa egal a 68 J
Modil Young la	200 GPa
Fòs ranpe (100,000h nan 650 degre)	35 MPa
Limit Fatig (107sik)	240 MPa

🔬 Pwopriyete Fizik

Pwopriyete	Valè
Dansite	7.90 g/cm³
Pwen k ap fonn	1400-1450 degre
Kondiktivite tèmik (20 degre)	16.3 W/m·K
Kondiktivite tèmik (100 degre)	17.8 W/m·K
Ekspansyon tèmik (20-100 degre)	17.2×10-6/K
Ekspansyon tèmik (20-500 degre)	18.4×10-6/K
Kapasite Chalè Espesifik	500 J/kg·K
Rezistans elektrik (20 degre)	0.72 µΩ·m
Pèmeyabilite mayetik	1.02 µr (Non-mayetik)
Tanperati Curie	Ki pa-mayetik

📏 Espesifikasyon pwodwi yo

Spesifikasyon	Opsyon ki disponib
Fòm pwodwi	Ba, baton, plak, fèy, tib, tiyo, Forgings, Distribisyon
Ranje dyamèt ba	6mm - 300mm
Plak epesè Range	3mm - 150mm
Ranje epesè fèy	0.5mm - 6mm
Dyamèt Eksteryè Tib	6mm - 219mm
Konfòmite estanda	ASTM A240, A479, A312, EN 10088-2, JIS G4304, GB/T 1220
Fini andigman	Cho woule, frèt woule, 2B, BA, No.4, HL, glas
Dimansyon tolerans	± 0.1mm a ± 0.5mm (depann sou fòm ak gwosè)
Opsyon Longè	Longè estanda oswa koupe nan espesifikasyon kliyan yo