AISI 316L se yon asye pur austenitic ki ba-kabòn
Mar 18, 2026
Kite yon mesaj
🧪 Konpozisyon Chimik
| Eleman | Konpozisyon (%) |
|---|---|
| Kabòn (C) | Mwens pase oswa egal a 0.030 |
| Manganèz (Mn) | Mwens pase oswa egal a 2.00 |
| Silisyòm (Si) | Mwens pase oswa egal a 0.75 |
| Fosfò (P) | Mwens pase oswa egal a 0.045 |
| Souf (S) | Mwens pase oswa egal a 0.030 |
| Kwòm (Cr) | 16.00 - 18.00 |
| Nikèl (Ni) | 10.00 - 14.00 |
| Molybdène (Mo) | 2.00 - 3.00 |
| Azòt (N) | Mwens pase oswa egal a 0.10 |
| Fè (Fe) | Balans |
⚙️ Pwopriyete mekanik
| Pwopriyete | Valè |
|---|---|
| Fòs rupture (Rm) | 485 - 620 MPa |
| Fòs Sede (Rp0.2) | Pi gran pase oswa egal a 205 MPa |
| elongasyon (A50mm) | Pi gran pase oswa egal a 40% |
| Dite (HRB) | Mwens pase oswa egal a 95 |
| Dite (HV) | 200 - 250 |
| Enèji enpak (KV) | Pi gran pase oswa egal a 60 J (nan 20 degre) |
| Modil Young la | 200 GPa |
| Limit fatig | 245 MPa (107sik) |
| Pwopòsyon Poisson a | 0.27 - 0.30 |
🔬 Pwopriyete Fizik
| Pwopriyete | Valè |
|---|---|
| Dansite | 8.00 g/cm³ |
| Pwen k ap fonn | 1400 - 1450 degre |
| Kondiktivite tèmik (20 degre) | 16.3 W/m·K |
| Kondiktivite tèmik (100 degre) | 18.3 W/m·K |
| Ekspansyon tèmik (20-100 degre) | 16.0×10-6/K |
| Ekspansyon tèmik (20-300 degre) | 17.0×10-6/K |
| Kapasite Chalè Espesifik | 500 J/kg·K |
| Rezistans elektrik (20 degre) | 0.74 µΩ·m |
| Pèmeyabilite mayetik | 1.02 µr (Non-mayetik) |
| Tanperati Curie | Ki pa-mayetik |