316L Nerjaveèi - Kowozyon Rezistan
Feb 26, 2026
Kite yon mesaj
Konpozisyon chimik nan asye pur 316
Tablo 1.Konpozisyon chimik tipik pou 316 alyaj asye pur
% | 316 | 316L | 316H | 316Ti |
C | 0.0-0.07 | 0.0-0.03 | 0.04-0.08 | 0.0- 0.08 |
Mn | 0.0-2.0 | 0-2.0 | 0.0-2.00 | 0.0-2.00 |
Si | 0.0-1.0 | 0.0-1.00 | 0.0-1.00 | 0.0- 1.00 |
P | 0.0-0.05 | 0.0-0.05 | 0-0.04 | 0.0-0.05 |
S | 0.0-0.02 | 0.0-0.02 | 0.0-0.02 | 0.0-0.03 |
Kr | 16.50-18.50 | 16.50-18.50 | 16.50-18.50 | 16.50- 18.50 |
Mo | 2.00-2.50 | 2.00-2.50 | 2.00-2.50 | 2.00- 2.50 |
Ni | 10.00-13.00 | 10.00-13.00 | 10.00-13.00 | 10.50- 14.00 |
Ti | - | - | - | 0.40- 0.70 |
Fe | balans | balans | balans | balans |
Pwopriyete asye pur 316
Pwopriyete mekanik nan asye pur 316
Tablo 2.Pwopriyete mekanik tipik pou 316 alyaj asye pur
Klas | 316 Bar ak Seksyon (jiska 160 mm epè) | 316 Fèy (jiska 8 mm epè) | 316 Plak (8 - 75 mm epesè) | 316L Bar ak Seksyon (jiska 160 mm) | Fèy 316L (jiska 8 mm epè) | 316 L plak (8 - 75 mm epesè) | 316H Bar (jiska 160 mm) | 316Ti Bar(jiska 160 mm) |
Fòs rupture (MPa) | 500 - 700 | 530 - 680 | 520 - 670 | 500 - 700 | 530 - 680 | 520 - 670 | 490 - 690 | 500 - 700 |
Prèv estrès (MPa) | 200 min | 240 min | 220 min | 200 min | 240 min | 220 min | 205 min | 200 min |
Elongasyon A50 mm | 40 min % | 40 min % | 45 min % | 40 min % | 40 min % | 45 min % | 35 % | 40 min % |
Dite Brinell | 215 Max HB | - | - | 215 Max HB | - | - | - | 215 Max HB |