Konpozisyon chimik nan asye pur 304
Tablo 1.Konpozisyon chimik pou 304 alyaj asye pur
|
% |
304 |
304L |
304H |
|
C |
0.0 - 0.07 |
0.0 - 0.03 |
0.04 - 0.08 |
|
Mn |
0.0 - 2.0 |
0.0 - 2.00 |
0.0 - 2.0 |
|
Si |
0.0 - 1.00 |
0.0 - 1.00 |
0.0 - 1.0 |
|
P |
0.0 - 0.05 |
0.0 - 0.05 |
0.0 - 0.04 |
|
S |
0.0 - 0.03 |
0.0 - 0.02 |
0.0 - 0.02 |
|
Kr |
17.50 - 19.50 |
17.50 - 19.50 |
17.00 - 19.00 |
|
Ni |
8.00 - 10.50 |
8.00 - 10.50 |
8.00 - 11.00 |
|
Fe |
Balans |
Balans |
Balans |
|
N |
0.0-0.11 |
0.0-0.11 |
0.0 - 0.10 |
Pwopriyete asye pur 304
Pwopriyete mekanik nan asye pur 304
Tablo 2a.Pwopriyete mekanik pou 304 alyaj asye pur - fèy jiska 8 mm epè
|
Klas |
304 |
304L |
304H |
|
Fòs rupture (MPa) |
540 - 750 |
520 - 700 |
- |
|
Prèv estrès (MPa) |
230 Min |
220 min |
- |
|
Elongasyon A50 mm |
45 min % |
45 min % |
- |
Tablo 2b.Pwopriyete mekanik pou 304 alyaj asye pur - plak soti nan 8 - 75 mm epè
|
Klas |
304 |
304L |
304H |
|
Fòs rupture (MPa) |
520 - 720 |
500 - 700 |
- |
|
Prèv estrès (MPa) |
210 min |
200 min |
- |
|
Elongasyon A5 |
45 min % |
45 min % |
- |
Tablo 2c.Pwopriyete mekanik pou 304 alyaj asye pur - ba ak seksyon jiska 160 mm dyamèt / epesè
|
Klas |
304 |
304L |
304H |
|
Fòs rupture (MPa) |
500 - 700 |
500 - 700 |
500 - 700 |
|
Prèv estrès (MPa) |
190 |
175 Min |
185 Min |
|
Elongasyon A50 mm |
45 min % |
45 min % |
40 min % |
|
Dite Brinell |
215 Max HB |
215 Max HB |
- |